TPEE Raw Material For Car Industrial Use Exceptional High-Temperature Resistance Superior Flex Fatigue Resistance Thermoplastic Polyester Elastomer
Features:
exceptional high-temperature resistance
superior flex fatigue resistance
good elastic recovery
broad low-temperature toughness
excellent oil and chemical resistance
Applications:
TPEE material bridges the performance gap between rubber, engineering plastics, and general-purpose TPEs. It is particularly well-suited for applications requiring high temperatures, dynamic stresses (repeated bending and twisting), and oily environments, playing a crucial role in the automotive industry.
Automotive Industry: This is the largest application market.
Various dust covers and boots (constant velocity joint dust covers, shock absorber dust covers, steering rack dust covers, ball joint dust covers)
Air lines, vacuum brake lines, turbocharger lines, fuel lines (inner or outer layers)
Seals (oil seals, air seals), gaskets
Interior components (parts requiring a soft touch)
Airbag cover materials
Electronic appliances:
Wire and cable jackets (requires heat resistance, oil resistance, flame retardancy, and flexibility)
Connector seals, plug jackets
Mobile phone antenna covers Adhesives, buttons
Industrial products:
Hydraulic hoses, pneumatic hoses
Transmission belts, timing belt tooth surface materials
Sealing strips, gaskets
Industrial hoses, bellows
Sports equipment handle rubber coating
Consumer products:
Sports equipment (ski boot buckles, carabiners, bicycle grips, racket handles)
Shoe materials (sole and upper materials, especially those requiring high elasticity and low-temperature toughness)
Tool handles (providing shock absorption and a comfortable grip)
Personal care products (toothbrush handle rubber coating)
Datasheet:
| Test Items |
Test method |
Test Unit |
Test Results |
| Malt Index |
ISO 1133 |
g/10min |
28/230℃/2.16KG |
| Flexural modulus |
ISO 178 |
Mpa |
220 |
| Tensile strength |
ISO 527 |
Mpa |
40 |
| 5% Tensile strength |
ISO 527 |
Mpa |
8.5 |
| 10%Tensile strength |
ISO 527 |
Mpa |
12.5 |
| 50%Tensile strength |
ISO 527 |
Mpa |
16 |
| Breaking elongation |
ISO 527 |
% |
650 |
| Hardness, 1S |
ISO R 868 |
D |
58 |
| Hardness, 15S |
ISO R 868 |
D |
54 |
| Izod notched impact(+23℃) |
ISO 180 |
KJ/㎡ |
NB |
| Izod notched impact(-30℃) |
ISO 180 |
KJ/㎡ |
NB |
| Malt Temperature(20℃/min) |
ISO 11357 |
215 |
℃ |
| UL Flame retartdant level ,1.60mm |
UL94 |
class |
HB |
| Water absorption,24h |
ISO 62 |
% |
0.5 |
| Shrinkage rate |
ISO 294 |
% |
1.6 |
| |
| Production Process: |
Drying material requirements: Please dry at 100-110℃ for 3-4 hours;
Injection molding temperature:
Melt temperature: 215 to 240℃
Barrel temperature:225 to 240℃
Die temperature:230 to 245℃
Mold temperature: 40 to 70 ℃
Pressure: 75-110 Pa |